Feartan magnetach iarann-teilgte liath

Coimeas Iarainn Liath				Microstructure （Mìrean tomhas-lìonaidh） (％)
Sìona (GB/T 9439)	ISO 185	ASTM A48/A48M	EN 1561	Structar Matrix
HT100 (HT10-26)	100	Àir.20 F11401	EN-GJL-100	Pearlite: 30-70％, flakes garbh; Ferrite: 30-70％; Eutectic fosfair dà-chànanach: ＜7％
HT150 (HT15-33)	150	Àir.25A F11701	EN-GJL-150	Pearlite: 40-90％, flakes garbh meadhanach; Ferrite: 10-60％; Eutectic fosfair dà-chànanach: ＜7％
HT200 (HT20-40)	200	Àir.30A F12101	EN-GJL-200	Pearlite: ＞95％, flakes meadhanach; Ferrite＜5％; Eutectic fosfair dà-chànanach ＜4％
HT250 (HT25-47)	250	Àir.35A F12401 Àir.40A F12801	EN-GJL-250	Pearlite: ＞98％ flakes tana meadhanach; Eutectic fosfair dà-chànanach: ＜2％
HT300 (HT30-54)	300	Àir.45A F13301	EN-GJL-300	Pearlite: ＞98％ flakes tana meadhanach; Eutectic fosfair dà-chànanach: ＜2％
HT350 (HT35-61)	350	Àir.50A F13501	EN-GJL-350	Pearlite: ＞98％ flakes tana meadhanach; Eutectic fosfair dà-chànanach: ＜1％

 

Tha feartan magnetach iarann ​​​​glas ag atharrachadh gu farsaing, bho permeability ìosal agus feachd co-èigneachail àrd gu permeability àrd agus feachd co-èigneachail ìosal. Tha na h-atharrachaidhean sin gu mòr an urra ri microstructure iarann ​​​​teilgte glas. Thathas a’ coileanadh eileamaidean alloying gus na feartan magnetach a tha a dhìth fhaighinn le bhith ag atharrachadh structar iarann ​​​​teilgthe glas.

Tha permeability magnetach àrd agus call hysteresis ìosal aig Ferrite; tha pearlite dìreach an aghaidh, tha permeability magnetach ìosal aige agus call mòr hysteresis. Tha Pearlite air a chruthachadh gu bhith na ferrite le bhith a’ annealing làimhseachadh teas, a dh’ fhaodadh an permeability magnetach àrdachadh ceithir tursan. Faodaidh meudachadh gràinean ferrite lùghdachadh a dhèanamh air call hysteresis. Lùghdaichidh làthaireachd cementite an dùmhlachd flux magnetach, permeability agus remanence, agus aig an aon àm a’ meudachadh permeability agus call hysteresis. Bidh làthaireachd grafait garbh a 'lùghdachadh na tha air fhàgail. Faodaidh an atharrachadh bho ghrafite seòrsa A (graifit ann an cumadh flake a tha air a chuairteachadh gu co-ionann gun stiùireadh) gu grafait seòrsa D (grafait air a lùbadh gu grinn le cuairteachadh neo-stiùiridh eadar dendrites) àrdachadh mòr a thoirt air an inntrigeadh magnetach agus feachd co-èigneachail. .

Mus ruig e an teòthachd èiginneach neo-magnetach, bidh an àrdachadh teòthachd ag àrdachadh gu mòr an permeability magnetach de iarann ​​​​teinnteach glas. Is e puing Curie de iarann ​​​​fìor-ghlan an teòthachd gluasaid α-γ de 770 ° C. Nuair a tha an ceudad mòr de silicon aig 5%, ruigidh puing Curie 730 ° C. Is e teòthachd puing Curie de cementite gun silicon 205-220 ° C.

Is e pearlite sa mhòr-chuid structar matrix de ìrean àbhaisteach de iarann ​​​​teilgte glas, agus tha an permeability as àirde aca eadar 309-400 μH / m.

 

Feartan magnetach iarann-teilgte liath
Còd Iarainn Liath	Co-dhèanamh ceimigeach (%)
	C	Si	Mn	S	P	Ni	Cr
A	3.12	2.22	0.67	0.067	0.13	＜0.03	0.04
B	3.30	2.04	0.52	0.065	1.03	0.34	0.25
C	3.34	0.83 - 0.91	0.20 - 0.33	0.021 - 0.038	0.025 - 0.048	0.04	＜0.02
Feartan magnetach		A		B		C
		Pearlite	Ferrite	Pearlite	Ferrite	Pearlite	Ferrite
Carbide carbon w (%)		0.70	0.06	0.77	0.11	0.88	/
Faireachdainn / T		0.413	0.435	0.492	0.439	0.5215	0.6185
Feachd Co-èigneachail / A•m-1		557	199	716	279	637	199
call hysteresis / J•m-3•Hz-1 (B=1T)		2696	-696	2729	1193	2645	938
Neart raon magnetach / kA•m-1 (B=1T)		15.9	-5.9	8.7	8.0	6.2	4.4
Max. Permeability magnetach / μH•m-1		396	1960	353	955	400	1703
Neart achadh magnetach nuair a bhios Max. Permeability magnetach / A•m-1		637	199	1035	318	1114	239
Resistivity / μΩ•m		0.73	0.71	0.77	0.75	0.42	0.37

 

Seo na leanas na feartan meacanaigeach aig iarann ​​​​teilgte glas:

Feartan meacanaigeach de iarann ​​​​teilgte liath
Nì a rèir DIN EN 1561	Tomhais	Aonad	EN-GJL-150	EN-GJL-200	EN-GJL-250	EN-GJL-300	EN-GJL-350
			EN-JL 1020	EN-JL 1030	EN-JL 1040	EN-JL 1050	EN-JL 1060
Neart tensile	Rm	MPA	150-250	200-300	250-350	300-400	350-450
0.1% Neart toraidh	Rp0,1	MPA	98-165	130-195	165-228	195-260	228-285
Neart leudachaidh	A	%	0,3-0,8	0,3-0,8	0,3-0,8	0,3-0,8	0,3-0,8
Neart teannachaidh	dB	MPa	600	720	840	960	1080
0,1% Neart teannachaidh	d0,1	MPa	195	260	325	390	455
Neart sùbailte	σbb	MPa	250	290	340	390	490
Schuifspanning	σaB	MPa	170	230	290	345	400
Strus rùsgadh	TtB	MPa	170	230	290	345	400
Modalan elasticity	E	GPa	78-103	88-113	103-118	108-137	123-143
Àireamh Poisson	v	-	0,26	0,26	0,26	0,26	0,26
Brinell cruas		HB	160-190	180-220	190-230	200 – 240	210-250
Dleasdanas	bW	MPa	70	90	120	140	145
Atharrachadh teannachaidh agus cuideam	ùsdW	MPa	40	50	60	75	85
Briseadh Neart	Klc	N/mm3/2	320	400	480	560	650
Dùmhlachd		g/cm3	7,10	7,15	7,20	7,25	7,30